Aluminum Sheet Metal
3003 Aluminum Sheet
3003 Aluminum Sheet
♦ Loading Port : Shanghai , Qingdao , Guangzhou , China
♦ Free Sample : A4 type
♦ Payment terms : L/C , D/P , T/T
| QTY(ton) | 3-5 | 10 | 20 | >20 |
|---|---|---|---|---|
| Est. time (days) | 5 | 7 | 15 | Negotiable |
♦ Certificated : ISO9001 ISO14001 TF16949
3003 aluminum sheet is a common product of aluminum-manganese alloy series.Due to the manganese alloy element, this product has excellent anti-rust characteristics, also known as anti-rust aluminum plate.
Commonly used for welding parts for ships, vehicles, automobiles and aircraft, pressure vessels requiring strict fire prevention, cooling devices, television towers, drilling equipment, transportation equipment, missile components, armor, etc
Product abilities
Thickness
0.2 – 6.0mm
Temper
F
O
H1X
H2X
Width
50 – 2450mm
Manufacturing technique
Direct Casting & Hot rolling
Continues Casting & Cold rolling
Surface Treatment
Plate
Plain sheet
Plain sheet with a PVC coating on one side
Stucco sheet
Stucco sheet with a PVC coating on one side
Performable Standard
GB/T 3880.1 – 2012
ASTM B209M
EN 485
YS – T 90 – 2009
Customizable product standards
Package
| Chemical Element | % Present |
|---|---|
| Manganese (Mn) | 1.00 – 1.50 |
| Iron (Fe) | 0.00 – 0.70 |
| Copper (Cu) | 0.05 – 0.20 |
| Magnesium (Mg) | – |
| Silicon (Si) | 0.00 – 0.60 |
| Zinc (Zn) | 0.00 – 0.10 |
| Titanium (Ti) | – |
| Other (Each) | 0.00 – 0.05 |
| Aluminium (Al) | Balance |
| Physical Property | Value |
|---|---|
| Density | 2.73 g/cm³ |
| Melting Point | 640 °C |
| Thermal Expansion | 23.0 x10^-6 /K |
| Modulus of Elasticity | 69 GPa |
| Thermal Conductivity | 180 W/m.K |
| Electrical Resistivity | 0.0349 x10^-6 Ω .m |
| Mechanical Property | Value |
|---|---|
| Tensile Strength | 145 – 195 MPa |
| Proof Stress | 125 Min MPa |
| Hardness Brinell | 42 HB |
| Elongation A | 10 Min % |