Aluminum Sheet Metal
3105 Aluminum Sheet
3105 Aluminum Sheet
♦ Loading Port : Shanghai , Qingdao , Guangzhou , China
♦ Free Sample : A4 type
♦ Payment terms : L/C , D/P , T/T
| QTY(ton) | 3-5 | 10 | 20 | >20 |
|---|---|---|---|---|
| Est. time (days) | 5 | 7 | 15 | Negotiable |
♦ Certificated : ISO9001 ISO14001 TF16949
3105 aluminium sheet is essentially a 98% aluminum alloy with minor additions to increase strength over that of alloy 1100 and 3003. It is not hardenable by heat treatment and it has good corrosion resistance, formability and weldability.
Typical applications include general sheet metal work requiring greater strength than is provided by 1000 series aluminum alloys, residential siding, mobile homes and sign making.
Product abilities
Thickness
0.2 – 6.0mm
Temper
O
H14
H16
H18
H24
Width
50 – 2450mm
Manufacturing technique
Direct Casting & Hot rolling
Continues Casting & Cold rolling
Surface Treatment
Plate
Plain sheet
Plain sheet with a PVC coating on one side
Stucco sheet
Stucco sheet with a PVC coating on one side
Performable Standard
GB/T 3880.1 – 2012
ASTM B209M
EN 485
YS – T 90 – 2009
Customizable product standards
Package
| Chemical Element | % Present |
|---|---|
| Manganese (Mn) | 0.30 – 0.80 |
| Iron (Fe) | 0.00 – 0.70 |
| Copper (Cu) | 0.00 – 0.30 |
| Magnesium (Mg) | 0.20 – 0.80 |
| Silicon (Si) | 0.00 – 0.60 |
| Zinc (Zn) | 0.00 – 0.40 |
| Titanium (Ti) | 0.00 – 0.10 |
| Other (Each) | 0.00 – 0.05 |
| Aluminium (Al) | Balance |
| Physical Property | Value |
|---|---|
| Density | 2.72 g/cm³ |
| Melting Point | 630 °C |
| Thermal Expansion | 24 .0x10^-6 /K |
| Modulus of Elasticity | 69 GPa |
| Thermal Conductivity | 173 W/m.K |
| Electrical Resistivity | 0.0382 x10^-6 Ω .m |
| Mechanical Property | Value |
|---|---|
| Tensile Strength | 150 – 200 MPa |
| Proof Stress | 130 Min MPa |
| Hardness Brinell | 48 HB |
| Elongation A | 7 Min % |