Aluminum Sheet Metal
5005 Aluminum Sheet
5005 Aluminum Sheet
♦ Loading Port : Shanghai , Qingdao , Guangzhou , China
♦ Free Sample : A4 type
♦ Payment terms : L/C , D/P , T/T
♦ MOQ:
| QTY(ton) | 3-5 | 10 | 20 | >20 |
|---|---|---|---|---|
| Est. time (days) | 5 | 7 | 15 | Negotiable |
♦ Certificated : ISO9001 ISO14001 TF16949
5005 aluminum alloy is similar to the 3005 alloy, with moderate strength and good corrosion resistance.
5005 aluminum sheet can be used as conductor, cooker, instrument panel, building decoration, etc.
Product abilities
Thickness
0.2 – 6.0mm
Temper
O
H2X
H3X
Width
50 – 2450mm
Manufacturing technique
Direct Casting & Hot rolling
Surface Treatment
Plate
Plain sheet
Plain sheet with a PVC coating on one side
Performable Standard
GB/T 3880.1 – 2012
ASTM B209M
EN 485
YS – T 90 – 2009
Customizable product standards
Package
| Chemical Element | % Present |
|---|---|
| Manganese (Mn) | 0.00 – 0.20 |
| Iron (Fe) | 0.00 – 0.70 |
| Copper (Cu) | 0.00 – 0.20 |
| Magnesium (Mg) | 0.50 – 1.10 |
| Silicon (Si) | 0.00 – 0.30 |
| Zinc (Zn) | 0.00 – 0.25 |
| Chromium (Cr) | 0.00 – 0.10 |
| Titanium (Ti) | – |
| Other (Each) | 0.00 – 0.05 |
| Aluminium (Al) | Balance |
| Physical Property | Value |
|---|---|
| Density | 2.7 g/cm³ |
| Melting Point | 630 °C |
| Thermal Expansion | 24.0 x10^-6 /K |
| Modulus of Elasticity | 68 GPa |
| Thermal Conductivity | 200 W/m.K |
| Electrical Resistivity | 0.0332 x10^-6 Ω .m |
| Mechanical Property | Value |
|---|---|
| Tensile Strength | 125 – 165 MPa |
| Proof Stress | 80 Min MPa |
| Hardness Brinell | 37 HB |
| Elongation A | 12 Min % |