6061 alloy has good plasticity and excellent corrosion resistance. In particular, no stress corrosion cracking tendency, its good welding, corrosion resistance and cold processing.
6061 aluminum plate is applied to all kinds of industrial structural parts that require certain strength, weldability and high corrosion resistance, such as truck manufacturing, building, ship, trolley, furniture, mechanical parts, precision processing, etc.
Product abilities
Thickness
0.2 – 100.0mm
Temper
F
O
H11X
T4
T6
T651
Width
50 – 2450mm
Manufacturing technique
Direct Casting & Hot rolling
Heat Treating
Pre-stretching
Surface Treatment
Plate
Plate with a PVC coating on one side
Plain sheet
Plain sheet with a PVC coating on one side
5 bar embossed
5 bar embossed sheet with a PVC coating on one side
Performable Standard
GB/T 3880.1 – 2012
ASTM B209M
EN 485
YS – T 90 – 2009
Customizable product standards
Package
| Chemical Element | % Present |
|---|---|
| Manganese (Mn) | 0.00 – 0.15 |
| Iron (Fe) | 0.00 – 0.70 |
| Copper (Cu) | 0.15 – 0.40 |
| Magnesium (Mg) | 0.80 – 1.20 |
| Silicon (Si) | 0.40 – 0.80 |
| Chromium (Cr) | 0.04 – 0.35 |
| Zinc (Zn) | 0.00 – 0.25 |
| Titanium (Ti) | 0.00 – 0.15 |
| Other (Each) | 0.00 – 0.05 |
| Aluminium (Al) | Balance |
| Physical Property | Value |
|---|---|
| Density | 2.7 g/cm³ |
| Melting Point | 580 °C |
| Thermal Expansion | 24.0 x10^- 6 /K |
| Modulus of Elasticity | 69 GPa |
| Thermal Conductivity | 170 W/m.K |
| Electrical Resistivity | 0.0400 x10^-6 Ω .m |
| Mechanical Property | Value |
|---|---|
| Tensile Strength | 290 Min MPa |
| Proof Stress | 240 Min MPa |
| Hardness Brinell | 93 HB |
| Elongation A | 12 Min % |